The use of stainless steel pipes is now more and more extensive. Because of its good corrosion resistance, it plays a crucial role in engineering construction. In the process of production, we need to perform solution treatment on stainless steel pipes. The main purpose is to obtain certain Martensite increases the hardness of the product. Let's take a look at the solution treatment of stainless steel pipes:
(1) The intermediate aging method is heated to (760±15) degree after the solution treatment, and the temperature is kept for 90 minutes because Cr23C6 carbides are precipitated from the austenite, which reduces the carbon and alloying elements content in the austenitic 904L stainless steel pipe , the Ms point is raised to 70 degree and then cooled to room temperature to obtain martensite plus ferrite plus retained austenite structure, and the retained austenite is decomposed after aging at 510 degree .
(2) 고온 조정 및 극저온 처리 후 용액을 먼저 950도까지 90분간 가열한다. Ms 포인트의 증가로 인해 실온으로 냉각하면 소량의 마르텐사이트를 얻을 수 있습니다. 마르텐사이트 양.
(3) 냉간변형법에 의한 용체화 처리 후, 상온에서 냉간변형을 한다. 냉간 변형 시 904L 이음매 없는 관에 형성되는 마르텐사이트의 양은 변형량 및 904L 스테인리스 강관의 조성과 관련이 있습니다.
위의 세 가지 방법은 일반적으로 스테인리스 강관의 용체화 처리에 사용되는 방법입니다. 그들이 당신을 도울 수 있기를 바랍니다.